Let’s Spray Tamco HP-662 2k Epoxy Black - HP660C , preheated w/ LumaIII Shadow

Описание: Applicable Substrates: Aluminum
Titanium
Stainless steel
Copper
Steel
Magnesium
Bronze
Nickel
(See our tech sheet on priming over rust)
Nickel Chrome plating
Ferrous and nonferrous alloy etc.
Plastics and rubber
Glass
Fiberglass
ABS
Over filler sanded with 80 grit or finer
Rust - Must be 2.5 mil film or higher
Surface Preparation: Metals: Throughly cleaned with HR397 wax and grease remover and wipe dry with clean
cloth.
Recoat: 1 hour
Plastics: Clean with HR397 using a Scotch-Brite pad, wipe dry with clean cloth.
Mix Ratio: Component Volume
HP661/HP662/HP663
HH660C
HR1360/1370/1380
Primer
1
Activator
1
Reducer
up to 5-10% (if needed)
Air Pressure &
Gun Setups:
Gun Setups:
See manufacturers suggestions Common User Suggestions: 1.3-1.5
1.3-1.5 mm fluid tip
35-40 PSI at the gun
8-10 PSI at the gun cap
8-10 PSI at the gun cap
(See your HVLP gun manufacture for specific setups for sealers)
[email protected] www.TamcoPaint.com (757) 627-9551 2-4
DIRECT TO ANYTHING EPOXY PRIMER
HP661/HP662/HP663
Application:
Do not use any metal prep conditioners, converters or any rust removers under this
product. They can cause failure.
Clean surface thoroughly using HR397 or HR397W Cleaner.
Sand area with 80-180 grit and re-clean with HR398.
Apply 1-2 medium-wet coats of DTA, waiting 20-30 minutes flash time between coats at
78°F.
Do not topcoat for at least 12 hours at 78°F.
Do not try to sand before 24 hours at 78°F
Induction period - not needed.
Pot Life: 12-18 hours at 70°F.
Do not use if shop temperature is less than 60°F (10°C).
Heat up your space & substrates.
Drying Times:
Air Dry at 78° 12-24hours.
Do not bake.
Recoat: Can be recoated at any time within 14 days without sanding.
Polishing:
N/A
Tamco® Tips: 1.In application, apply as a primer sealer. DTA is not a building primer. (Use HP770
series for build).
2.DTA is very slow curing, allow a day or longer to dry before top coating.
3.Heavy coats , over applying, or not waiting the proper flash times can cause severe
"wrinkling"
.
4.If you choose to sand, sand with 320-400 grit sandpaper.
5.For maximum corrosion resistance, two medium coats should be applied.
6.Applying over rust, you must have 2.5 mil film or higher.
7.Heat up your space & substrates for best adhesion capabilities.
Equipment Cleaning:
Lacquer Thinner or HR1360 is an excellent cleaner.
Cold Shop Conditions:
Do not Spray below 65°F.
[email protected] www.TamcoPaint.com (757) 627-9551 3-4
DIRECT TO ANYTHING EPOXY PRIMER
HP661/HP662/HP663
TECHNICAL DATA & PHYSICAL PROPERTIES
Test Method: ASTM D 3359B
Dry Film Thickness (mil) recommended Mil: 1.2-2.0
Colors: Grey, White, Black
Mix Ratio: 1:1
Viscosity: (RTS) 18-22 sec. EZ Zahn #2
Theoretical Dry Film: 480 ft2 @ 1 Mil Weight Solids (RTS) 37%
Color & Gloss holdout: NA
Volume Solids: (RTS) 32%
Humidity Resistance: Excellent
Weight Per Gallon: White: 10.38lb Black: 9.59lb. Grey: 10.38lb.
Solvent Resistance: Excellent
Florida Exposure: NA
Package VOC: 3.10 # / gal
RTS VOC: 4.5# / gal
Chip Resistance: Good
See Safety Data Sheet/Material Safet